Differs from type WR in its putty and non-dripping consistency
and the mineral fillers. Due to these properties, this wear-
resistant type is mainly used where castable compounds cannot
be processed:
- for repairs on conveyors, guides and sliding ways
- where rolling or sliding movements cause wear
- to prevent wear on metal surfaces which are exposed to
extreme abrasion and erosion
- and as a wear-resistant under-coating before final coating
with WEICON Ceramic BL
| Item number | weicon 10350005 | | GTIN | 4024596002824 |
| Item features |
|---|
| Composition | Epoxy resin mineral-filled | | Specific Properties | putty, wear resistant | | Mixing ratio by weight % (Resin/Hardener) | 100:25 | | Pot-life at +20°C (200 g preparation) | 45 Min. | | Density of the mixture | 1,67 g/cm³ | | Viscosity of the mixture | 560.000 mPa·s | | Max. layer thickness per application | 10 mm | | Cure time mechanical loads | 16 h | | final hardness | 24 h | | Mean compressive strength (+25°C) acc. to DIN 53281-83 | 71 MPa | | Mean tensile strength (+25°C) acc. to DIN 53281-83 | 29 MPa | | Mean Flexural strength (+25°C) acc. to DIN 53281-83 | 39 MPa | | Mean strength E-Modul (+25°C) acc. to DIN 53281-83 | 2.500 - 3.000 MPa | | Shore D (+25°C) acc. to DIN 53281-83 | 82 | | Shrinkage | 0,025 % | | Thermoforming resistance | 65 °C | | Colour | dark-grey | | Temperature resistance | -35 bis +120 °C |
|