High-temperature resistant casting resin system especially for industrial
use. This type is non-corroding, anti-magnetic and cures practically
without shrinkage. The product provides high temperature resistance
after precuring at room temperature and post-curing (afterbake) at +120°C.
Especially suitable for:
- pouring out moulds (e.g. vacuum and foam moulds)
- making fixing devices and tools (e.g. injection dies)
which are exposed to high temperatures.

Purchase data
Item number	weicon 10100020
GTIN	4024596001100

Item features
Composition	Epoxy resin aluminiumfilled
Specific Properties	liquid, high-temp. resistant
Mixing ratio by weight % (Resin/Hardener)	100:8
Pot-life at +20°C (200 g preparation)	60 Min.
Density of the mixture	1,62 g/cm³
Viscosity of the mixture	25.000 mPa·s
Max. layer thickness per application	60 mm
Cure time mechanical loads	24 h
final hardness	48 h
Mean compressive strength (+25°C) acc. to DIN 53281-83	140 MPa
Mean tensile strength (+25°C) acc. to DIN 53281-83	25 MPa
Mean Flexural strength (+25°C) acc. to DIN 53281-83	77 MPa
Mean strength E-Modul (+25°C) acc. to DIN 53281-83	5.800 - 6.000 MPa
Shore D (+25°C) acc. to DIN 53281-83	90
Shrinkage	0,01 %
Thermoforming resistance	130 °C
Colour	grey
Temperature resistance	-35 bis +220 °C