Fast-curing construction adhesive for high-strength bonding with
high impact resistance, high peel and shear strength. Temperature
resistant from -50°C up to +130°C, briefly (30 minutes) up to +180°C.
Consists of adhesive and activator. Type with higher strength and
lower viscosity (liquid). To be processed in the easy no-mix procedure. | Item number | weicon 10563860 | | GTIN | 4024596034221 |
| Item features |
|---|
| Basis | Methyl methacrylate | | Properties | liquid | | Viscosity Adhesive | 4.500 mPa.s | | Viscosity Activator | very thin liquid mPa.s | | Specific weight Adhesive | 1,00 g/cm³ | | Specific weight Activator | 0,87 g/cm³ | | Colour adhesive | yellowish, transparent | | Colour activator | colourless, transparent | | Consumption adhesive (depending on surface structure) | 180 - 300 g/m² | | Consumption activator (depending on surface structure) | 30 - 150 g/m² | | Evaporation time activator at +20°C | 5 min. | | Effectiveness activator after application at +20°C | max. 30 days | | Processing temperature | +10 to +30 °C | | Curing temperature | +6 to +40 °C | | Gap covering power | max. 0,8 mm | | Handling strength (35% strength) after | 5 min. | | Mechanical durability (50% strength) after | 8 min. | | Final hardness (100%) strength after | 24 h | | Average tensile shear strength after 7 days with DIN 53281-83 | | | Aluminium, sand-blasted | 26 N/mm² | | Steel, sand-blasted | 25 N/mm² | | Stainless steel, sand-blasted | 25 N/mm² | | Copper, sand-blasted | 19 N/mm² | | Brass, sand-blasted | 26 N/mm² | | ABS, roughened | 6 N/mm² | | Hard PVC, roughened | 11 N/mm² | | GRP, roughened | 20 N/mm² | | Temperature resistance | -50 to +130, short-term up to +180 °C | | Peel resistance on aluminium | 6 N/mm | | Thermal conductivity | 0,2 W/m.K | | Dielectric strength | 10 kV/mm |
|