WEICON RK-1300, compl. 60 g Construction adhesive + activator,weicon 10560060 WEICON RK-1300, compl. 60 g Construction adhesive + activator |
Fast-curing construction adhesive for high-strength bonding with high
impact resistance, high peel and shear strength. Temperature resistant
from -50°C up to +130°C, briefly (30 minutes) up to +180°C. Consists
of adhesive and activator. To be processed in the easy no-mix
procedure. Preferably for metals and hard plastics. | Item number | weicon 10560060 | | GTIN | 4024596034214 |
| Item features |
|---|
| Basis | Methyl methacrylate | | Properties | pasty | | Viscosity Adhesive | 21.000 mPa.s | | Viscosity Activator | very thin liqiud mPa.s | | Specific weight Adhesive | 1,20 g/cm³ | | Specific weight Activator | 0,87 g/cm³ | | Colour adhesive | beige, opaque | | Colour activator | transparent, colourless | | Consumption adhesive (depending on surface structure) | 180 - 300 g/m² | | Consumption activator (depending on surface structure) | 30 - 150 g/m² | | Evaporation time activator at +20°C | 5 min. | | Effectiveness activator after application at +20°C | max. 30 days | | Processing temperature | +10 to +30 °C | | Curing temperature | +6 to +40 °C | | Gap covering power | max. 0,8 mm | | Handling strength (35% strength) after | 6 min. | | Mechanical durability (50% strength) after | 9 min. | | Final hardness (100%) strength after | 24 h | | Average tensile shear strength after 7 days with DIN 53281-83 | | | Aluminium, sand-blasted | 25 N/mm² | | Steel, sand-blasted | 21 N/mm² | | Stainless steel, sand-blasted | 26 N/mm² | | Copper, sand-blasted | 26 N/mm² | | Brass, sand-blasted | 25 N/mm² | | ABS, roughened | 6 N/mm² | | Hard PVC, roughened | 7 N/mm² | | GRP, roughened | 16 N/mm² | | Temperature resistance | -50 bis +130, short-term up to +180 °C | | Peel resistance on aluminium | 6 N/mm | | Thermal conductivity | 0,2 W/m.K | | Dielectric strength | 10 kV/mm |
|